Abstract In1xMnxSe x0 005 01and 015 thin films were evaporated by using thermal Essay

Abstract In1-xMnxSe (x=0, 0.05, 0.1and 0.15) thin films were evaporated by using thermal evaporation technique. Both of dispersion energy (Ed) and oscillating energy (Eo) were determined by applying single oscillator theory. The values of lattice dielectric constant (µL) and free carrier concentration/effective mass) (N/m*) were calculated. On the other hand, other important parameters such as, the values of first order of moment (M-1), the third order of moment (M-3) and static refractive index (no), were determined. The both of dielectric loss (µ) and dielectric tangent loss (µ\) for these films increased with photon energy and had a highest value near the energy gap Eg.

Also, the same behavior was noticed for the real part of optical conductivity (1) and imaginary part of optical conductivity (2), the relation between Volume Energy Loss Function (VELF) and Surface Energy Loss Function (SELF) were determined. The Linear optical susceptibility ((1)) increases with photon energy for all compositions. The nonlinear optical parameters such as, nonlinear refractive index (n2), the third-order nonlinear optical susceptibility ((3)), non-linear absorption coefficient (Іc) , were determined theoritically.

Don't use plagiarized sources. Get Your Custom Essay on
Abstract In1xMnxSe x0 005 01and 015 thin films were evaporated by using thermal Essay
From as low as $9/Page
Order Essay

Both of The electrical susceptibility (e) and relative permittivity (µr) increase with photon energy and had a highest value near the energy gap. The semiconducting results such as, density of the valence band, conduction band and Fermi level position (Ef) were calculated.Key words: In1-xMnxSe thin films, dielectrical results, semiconducting results, non- linear optical properties.Corresponding author: S.A.Gad E-mail: [email protected] AIIIBVI semiconductors such as, Ga1-xMnxS [1-3], Zn1€’xMnxSe [4], and finally In1-xMnxSe [5-7] had been studied widely, because of their applications such as, solar energy conversion [8″12], infrared devices [9], lasers [9], photovoltaic applications [13] diodes [14]. The structural and physical properties of InSe were investigated [15″18], InSe thin films had polycrystalline structure after heat treatment [19-22]. The optical properties of InSe thin films were studied [ 23-29], it was found that, InSe samples had an direct energy gap of 1.35 ± 0.02 eV [24], 1.10 eV[25], (2.5 to 3.34 eV)[26] and the values of (1.7, 1.2 and 1.1 eV)[17]. The electrical and dielectrical studies for InSe thin films and crystals were studied [30-35], the ac conductivity is decreased with frequency for InSe [30]. The temperature affect on ac conductivity [31-33], as a result of its strong electron interaction with holes [36]. On the other hand, MnSe had been studied widely, it was noticed that, MnSe crystals had hexagonal structure with lattice constant of (a=5.462 є) and (a=3.63 є; c=5.91 є) [37-39]. The optical properties of MnSe thin films had been studied [40-42], and was found that, MnSe had energy gap in the range of 1.13 ” 1.25 eV [40-41]. The electrical and dielectrical properties had been investigated [42-44], the electrical resistivity of MnSe decreased with temperature [44]. Furthermore, the transport and magnetic properties of In1-xMnxSe had been studied widely [7, 45-48], while, energy gap and structure dependence on composition of In1-xMnxSe thin films and bulk materials had been studied by many authors [49-50], it was found that, these studied thin films had an amorphous structure [49], the optical energy gap increases with the x value for both thin films bulk material [50]. The aim of the present work is studying the effect of the composition on dielectrical loss (µ) and dielectric tangent loss (µ\), both of real and imaginary part of optical conductivity(1, and 2) respectively, electrical susceptibility ((e)), linear optical susceptibility ((1)), the non-linear optical results such as, nonlinear refractive index (n2), nonlinear absorption coefficient (Іc), non-optical susceptibility ((3)), dielectrical results and finally electronic properties such as Fermi level position (Ef) and density of both of valence conduction band (Nv) and conduction band (Nc) of In1-xMnxSe thin films.3. Results and discussions3.1. Optical results The structure of these thin films with different compositions had an amorphous structure as investigated in previous work [49], The main optical measurements properties is that the optical transmittance, T and reflectance, R were measured and discussed in previous work [49]. The concept of the single oscillator theory was expressed by the Wemple”DiDomenico relationship [51]: (1)Where n is the refractive index values of these samples which is determined in previous work [49], E is the photon energy, Eo is the oscillator energy and Ed is the dispersion energy. The values of Eo and Ed for all samples are shown in table 1. Fig. 1 shows, the relation of n2 and “2 for the thin films in order to determine the effective mass ratio with the carrier concentration using the following equation [52]: (2)Where µL is the lattice dielectric constant, µo is the permittivity of free space, e is the charge of electron, n, k is the liner refractive index and the absorption index of these films respectively, which was determined in previous work [49], N is the free carrier concentration of theses investigated films, and c is the speed of light. From this Fig. the slope equal to the value of (e.N/4c2µom*), so the effective mass of these films was calculated as shown in table 1. From this table it was noticed that, the value of (x) affected on the ratio of (N/m*), the access of Mn, the access of electrons.The values of the first order of moment (M-1) and the third order of moment (M-3) derived from the relations [52]: (3) (4)Table 1 shows, the values of the M-1 and M-3 for these thin films. The oscillator strength f which was calculated as follow [53]: (5)The values of the f are shown in table 1. Another important parameter depending on both of Eo and Ed is that, static refractive index no which was determined using following equation [54]: (6)The values of no for all these samples are shown in table 1.3.2. Dielectric, optical conductivity and linear optical susceptibility resultsFig.2 represents the relation between (n2-1)-1 vs. (hЅ) for the thin films. It is shown that (n2-1)-1 increases as the Mn content increases. The dielectric loss µ and dielectric tangent loss µ\ for these films were calculated using the equations [55]: (7) (8) Figs 3(a,b) show both of µ and µ\ versus (hЅ) for all thin films. From this figure, it was seen that, the values of both µ and µ\ decreased with photon energy (hЅ) for all studied samples, and the peak maximum values position decreased with increasing Mn content, this is due to the increasing of electron motilities with x values, which caused a decreased in both of µ and µ\. The optical conductivity was calculated from the following equations [56]: (9) (10)Figs 4(a,b) show, the real part of optical conductivity (1) and imaginary part of optical conductivity (2) dependence on (hЅ) for these films. The behavior of both 1 and 2 for all these studied films is the same with (hЅ), by meaning that, all values of 1 and 2 increase with photon energy for all these samples. The values of Volume Energy Loss Function (VELF) and Surface Energy Loss Function (SELF) for these films were determined optically as follow [52]: (11) (12)The relation between VELF/SELF for these thin films is shown in Fig. 5. Linear optical susceptibility ((1)) describes the response of the material to an optical wave length, ((1)) was determined using the following relation [57]: (13)The relation between ((1)) and (hЅ) for In1-xMnxSe thin films with different concentration is shown in Fig.6, from this figure it was seen that, the linear optical susceptibility ((1)) increased with (hЅ).3.3. Nonlinear optical propertiesAn important parameter of the non-linear optical parameters is that the nonlinear refractive index (n2), which can be explained as, when light with high intensity propagates through a medium, this causes nonlinear effects[58], n2 was determined from the following simple equation [59-60]: (14)The dependence of n2 on wavelength for In1-xMnxSe thin films is shown in Fig. 7. The values of n2 decrease with wavelength for all these studied samples. An important parameter to assess the degree of nonlinearities is the third-order nonlinear optical susceptibility ((3)), which was determined using the following equation [61]: (15)Where A is a quantity that is assumed to be frequency independentand nearly the same for all materials =1.7 x 10-10 e.s.u [61]. The third-order nonlinear optical susceptibility 3 dependance on and photon energy for In1-xMnxSe thin films with different (x) values is shown in Fig.8. It was noticed that, the behavior of ((3)) is the same for all the studied samples, the values of ((3)) increses with (hЅ), this is due to, when (hЅ) incresed the defliction of the incident ligth beam increase . On the other hand, another important nonlinear parameter such was non-lnear absorption coefficient (Іc) which, determined as follows [62]: (16) Fig. 9 shows the influence of hЅ on (Іc). It is observed that, the values of Іc increses with hЅ for all these samples as shown in Fig. 9. Because of the higher values of (hЅ), the large number number of excited electron which overcome the band gap.3.4. Electrical results Electrical susceptibility ((e)) was determined using the following relation [63]: (17) Fig. 10 shows the electrical susceptibility ((e)) dependence on (hЅ) of these investigated samples. From this figure it is clear that, the values of ((e)) increase with (hЅ), this is due to, the electron mobility increases with (hЅ).The relative permittivity µr was calculated using the following relation [64] (18) The relation between relative permittivity (µr) and wavelength for In1-xMnxSe thin films with different (x) values is shown in Fig. 11. It is clear that, the values of (µr) increase with (hЅ) for all these samples; this could be attributed to, the electron mobility increases with (hЅ).3.5. Semiconducting and electronic resultsThe density of states (DOS) of a system describes the number of states per interval of energy at each energy level available to be occupied. The values of density for conduction and valence bands play very important rule of examination the linear optical transition and non-linear optical properties. The density of state for both the valence and conduction band was calculated using the following equations [65]:- (19) (20)Where Nv and Nc were the density of states for both valence and conduction bands respectively, effective mass of electrons m*e (InSe) = 0.14 [66], m*e (MnSe (= 0.15 [67], effective mass of holes m*h (InSe) = 0.37 [66] and K is a Boltzmann constant. The determined values for both Nv, Nc were shown in table 1. Another important factor was determined theoretically is the position of Fermi level [61]: (21)The values of Fermi level position for these investigated thin films are shown in table 1.4. ConclusionThe values of Ed and Eo for In1-xMnxSe increase with different x values (x=0.05, 0.1 and 0.15), and had the values (Ed from 4.22 to 4.80 eV) and also Eo had the values from (3.14 to 3.40 eV). The values of (N/m*) increased with x values (Mn content), which is due to the increase of free carrier. The values of M-1 and M-3 also increase with increasing Mn concentration. The values of no have a very slight increase with increasing Mn content. The values of both dielectric loss (µ) and dielectric tangent loss (µ\) increases with photon energy, the maximum values decrease with increase Mn content, due to the increase of electron mobility’s with increasing Mn ratio. The values of both (1) and (2) showed maximum values of these samples from (1.17 to 1.33 eV) with increasing Mn ratio. The Linear optical susceptibility ((1)) increases with photon energy for all compositions. The values of n2 increases with wavelength for all these samples, while the values of ((3)) increased with photon energy. This means that these samples had a high ability to changing its optical properties by changing wavelength and applied field. The non-linear absorption coefficient (Іc) increased with photon energy for these samples, also both of the electrical susceptibility ((e)) and relative permittivity (µr) increase with photon energy and had a highest value near the energy gap. The composition values (x) affected on the values of density of the valence band and conduction band, while Fermi level position Ef affected slightly with the composition values (x).

The Homework Writings
Order NOW For A 10% Discount!
Pages (550 words)
Approximate price: -

Our Advantages

Plagiarism Free Papers

All our papers are original and written from scratch. We will email you a plagiarism report alongside your completed paper once done.

Free Revisions

All papers are submitted ahead of time. We do this to allow you time to point out any area you would need revision on, and help you for free.

Title-page

A title page preceeds all your paper content. Here, you put all your personal information and this we give out for free.

Bibliography

Without a reference/bibliography page, any academic paper is incomplete and doesnt qualify for grading. We also offer this for free.

Originality & Security

At thehomeworkwritings.com, we take confidentiality seriously and all your personal information is stored safely and do not share it with third parties for any reasons whatsoever. Our work is original and we send plagiarism reports alongside every paper.

24/7 Customer Support

Our agents are online 24/7. Feel free to contact us through email or talk to our live agents.

Try it now!

Calculate the price of your order

We'll send you the first draft for approval by at
Total price:
$0.00

How it works?

Follow these simple steps to get your paper done

Place your order

Fill in the order form and provide all details of your assignment.

Proceed with the payment

Choose the payment system that suits you most.

Receive the final file

Once your paper is ready, we will email it to you.

Our Services

We work around the clock to see best customer experience.

Pricing

Flexible Pricing

Our prices are pocket friendly and you can do partial payments. When that is not enough, we have a free enquiry service.

Communication

Admission help & Client-Writer Contact

When you need to elaborate something further to your writer, we provide that button.

Deadlines

Paper Submission

We take deadlines seriously and our papers are submitted ahead of time. We are happy to assist you in case of any adjustments needed.

Reviews

Customer Feedback

Your feedback, good or bad is of great concern to us and we take it very seriously. We are, therefore, constantly adjusting our policies to ensure best customer/writer experience.